A very fast-curing, two-component hybrid polyurea system. It is an economical protection and coating solution for surfaces where the chemical resistance of pure polyurea is not required.
• Economical alternative to pure polyurea systems
• Very fast curing and commissioning
• 100% solid, VOC-free, odorless
• Excellent temperature stability
• Seamless and waterproof
• Excellent crack bridging property
• Excellent adhesion strength
• Very good tensile and structural strength
• Unaffected by moisture and temperature
• Possibility of coating in desired thickness
Chemical composition A: MDI Prepolymer - B: Amine Resin Mixing Ratio by Volume (lt) A=100 B=100
Volatile component content (%) ASTM D1259 0 Mixing Ratio by Weight (kg) A= 112 B= 100
Solid content (%) ASTM D2697 100 Application Temperature (°C) °C A: 70-80 B: 70-80
Gel time (s) ------ 5-10 Process Pressure (bar) Bar A: 150-200 B: 150-200
Skin setting time (s) ------ 15-45
Tensile strength (MPa) ASTM D638 ≥ 13
Module (MPa) ASTM D638 100% elongation ≥ 5
Elongation at break (%) ASTM D638 ≥400
Hardness (Shore A) ASTM D2240 80-85
Tear resistance (N/mm)
Taber abrasion resistance (mg)
ASTM D 624
EN ISO 5470-1
≥15
<150 (H22, 1000 rpm)
• Concrete surface coating
• Roof, balcony and terrace coatings
• Applications on fiberglass, polystyrene foam, polyurethane foam
Impact resistance EN ISO 6272-1 Class III
• ACTIVECOAT HB 201 : 200 kg
Adhesion strength (N/mm2) ASTM D 4541 Concrete: ≥2.5 Steel: ≥6
• ACTIVECOAT PRE 152: 220 kg
Fire resistance Class E (B2) TS EN13501-1 (DIN 4102)